| TYPICAL PROPERTIES (1) |
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 50 mm/min | 48 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 48 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 2200 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 82 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 82 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2060 | MPa | ASTM D 790 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23掳C | 3204 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23掳C | 534 | J/m | ASTM D 256 | |
| Gardner, 23掳C | 43 | J | ASTM D 3029 | |
| Modified Gardner, 23掳C | 43 | J | ASTM D 3029 | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 145 | 掳C | ASTM D 1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 99 | 掳C | ASTM D 648 | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 137 | 掳C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 98 | 掳C | ASTM D 648 | |
| CTE, -40掳C to 40掳C, flow | 9.18E-05 | 1/掳C | ASTM E 831 | |
| CTE, 60掳C to 138掳C, flow | 1.24E-04 | 1/掳C | ASTM E 831 | |
| Relative Temp Index, Elec | 120 | 掳C | UL 746B | |
| Relative Temp Index, Mech w/impact | 120 | 掳C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | 掳C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.34 | - | ASTM D 792 | |
| Specific Volume | 0.75 | cm鲁/g | ASTM D 792 | |
| Water Absorption, 24 hours | 0.08 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 0.75-2.3 mm | 0.8 - 1.1 | % | SABIC Method | |
| Mold Shrinkage, flow, 2.3-4.6 mm | 1 - 1.4 | % | SABIC Method | |
| Mold Shrinkage, xflow, 0.75-2.3 mm | 0.9 - 1.3 | % | SABIC Method | |
| Mold Shrinkage, xflow, 2.3-4.6 mm | 1.2 - 1.6 | % | SABIC Method | |
| Melt Flow Rate, 250掳C/5.0 kgf | 8 | g/10 min | ASTM D 1238 | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity | >1.2E+16 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in air, 3.2 mm | 18.5 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 25.1 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18.5 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 100 Hz | 3.2 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 3.2 | - | ASTM D 150 | |
| Dissipation Factor, 100 Hz | 0.003 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.03 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 | |