GELOY HRA170 is a high heat resistant ASA+PC. It shows high impact retention, which can be positioned for various outdoor and indoor applications requiring superior heat aging properties and colour stability. |
Property |
TYPICAL PROPERTIES(1) | ||||
MECHANICAL | Value | Unit | Standard | |
Taber Abrasion, CS-17, 1 kg | 95 | mg/1000cy | SABIC Method | |
Tensile Stress, yield, 5 mm/min | 55 | MPa | ISO 527 | |
Tensile Stress, break, 5 mm/min | 60 | MPa | ISO 527 | |
Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 | |
Tensile Stress, break, 50 mm/min | 62 | MPa | ISO 527 | |
Tensile Strain, yield, 5 mm/min | 5 | % | ISO 527 | |
Tensile Strain, break, 5 mm/min | 125 | % | ISO 527 | |
Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 | |
Tensile Strain, break, 50 mm/min | >50 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 | |
Flexural Stress, yield, 2 mm/min | 85 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 | |
Hardness, H358/30 | 106 | MPa | ISO 2039-1 | |
Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
IMPACT | Value | Unit | Standard | |
Izod Impact, notched 80*10*4 +23掳C | 60 | kJ/m虏 | ISO 180/1A | |
Izod Impact, notched 80*10*4 -30掳C | 15 | kJ/m虏 | ISO 180/1A | |
Charpy 23掳C, V-notch Edgew 80*10*4 sp=62mm | 60 | kJ/m虏 | ISO 179/1eA | |
Charpy -30掳C, V-notch Edgew 80*10*4 sp=62mm | 12 | kJ/m虏 | ISO 179/1eA | |
THERMAL | Value | Unit | Standard | |
Thermal Conductivity | 0.2 | W/m-掳C | ISO 8302 | |
CTE, 23掳C to 60掳C, flow | 8.E-05 | 1/掳C | ISO 11359-2 | |
Ball Pressure Test, 125掳C +/- 2掳C | PASSES | - | IEC 60695-10-2 | |
Vicat Softening Temp, Rate B/50 | 129 | 掳C | ISO 306 | |
Vicat Softening Temp, Rate B/120 | 132 | 掳C | ISO 306 | |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 121 | 掳C | ISO 75/Be | |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 112 | 掳C | ISO 75/Ae | |
PHYSICAL | Value | Unit | Standard | |
Mold Shrinkage on Tensile Bar, flow (2) | 0.4 - 0.6 | % | SABIC Method | |
Density | 1.15 | g/cm鲁 | ISO 1183 | |
Water Absorption, (23掳C/sat) | 0.6 | % | ISO 62 | |
Moisture Absorption (23掳C / 50% RH) | 0.2 | % | ISO 62 | |
Melt Volume Rate, MVR at 260掳C/5.0 kg | 17 | cm鲁/10 min | ISO 1133 | |
ELECTRICAL | Value | Unit | Standard | |
Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 | |
Relative Permittivity, 1 MHz | 2.8 | - | IEC 60250 | |
Dissipation Factor, 1 MHz | 0.013 | - | IEC 60250 | |
Comparative Tracking Index | 225 | V | IEC 60112 | |
FLAME CHARACTERISTICS | Value | Unit | Standard | |
UL Compliant, 94HB Flame Class Rating (3)(4) | 1.6 | mm | UL 94 by GE | |
Glow Wire Flammability Index 750掳C, passes at | 3.2 | mm | IEC 60695-2-12 | |
Oxygen Index (LOI) | 22 | % | ISO 4589 |
Source GMD, last updated:01/31/2001 |
Processing |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 100 - 110 | 掳C |
Drying Time | 2 - 4 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 260 - 290 | 掳C |
Nozzle Temperature | 240 - 280 | 掳C |
Front - Zone 3 Temperature | 250 - 290 | 掳C |
Middle - Zone 2 Temperature | 250 - 290 | 掳C |
Rear - Zone 1 Temperature | 230 - 260 | 掳C |
Hopper Temperature | 60 - 80 | 掳C |
Mold Temperature | 60 - 90 | 掳C |