Valox* Resin 420SE0 | Americas: COMMERCIAL |
30% GR, UL94V-0/5V rated. Numerous applications; edge trimmers, food mixer motor stator and commutator, cooling fan, connectors, bobbins, switches etc |
Property |
TYPICAL PROPERTIES(1) | ||||
MECHANICAL | Value | Unit | Standard | |
Tensile Stress, yld, Type I, 5 mm/min | 95 | MPa | ASTM D 638 | |
Tensile Stress, brk, Type I, 5 mm/min | 95 | MPa | ASTM D 638 | |
Tensile Strain, yld, Type I, 5 mm/min | 1.2 | % | ASTM D 638 | |
Tensile Strain, brk, Type I, 5 mm/min | 1.2 | % | ASTM D 638 | |
Tensile Modulus, 5 mm/min | 11500 | MPa | ASTM D 638 | |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 186 | MPa | ASTM D 790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 9400 | MPa | ASTM D 790 | |
Hardness, Rockwell R | 119 | - | ASTM D 785 | |
IMPACT | Value | Unit | Standard | |
Izod Impact, unnotched, 23掳C | 640 | J/m | ASTM D 4812 | |
Izod Impact, notched, 23掳C | 69 | J/m | ASTM D 256 | |
Izod Impact, notched, -30掳C | 64 | J/m | ASTM D 256 | |
Instrumented Impact Total Energy, 23掳C | 6 | J | ASTM D 3763 | |
THERMAL | Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50 | 200 | 掳C | ASTM D 1525 | |
HDT, 0.45 MPa, 3.2 mm, unannealed | 212 | 掳C | ASTM D 648 | |
HDT, 1.82 MPa, 3.2mm, unannealed | 200 | 掳C | ASTM D 648 | |
HDT, 0.45 MPa, 6.4 mm, unannealed | 215 | 掳C | ASTM D 648 | |
HDT, 1.82 MPa, 6.4 mm, unannealed | 204 | 掳C | ASTM D 648 | |
CTE, -40掳C to 40掳C, flow | 2.52E-05 | 1/掳C | ASTM E 831 | |
CTE, 60掳C to 138掳C, flow | 2.52E-05 | 1/掳C | ASTM E 831 | |
Relative Temp Index, Elec | 130 | 掳C | UL 746B | |
Relative Temp Index, Mech w/impact | 130 | 掳C | UL 746B | |
Relative Temp Index, Mech w/o impact | 140 | 掳C | UL 746B | |
PHYSICAL | Value | Unit | Standard | |
Specific Gravity | 1.61 | - | ASTM D 792 | |
Specific Volume | 0.62 | cm鲁/g | ASTM D 792 | |
Water Absorption, 24 hours | 0.06 | % | ASTM D 570 | |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC Method | |
Mold Shrinkage, flow, 1.5-3.2 mm | 0.3 - 0.5 | % | SABIC Method | |
Mold Shrinkage, flow, 3.2-4.6 mm | 0.5 - 0.8 | % | SABIC Method | |
Mold Shrinkage, xflow, 1.5-3.2 mm | 0.4 - 0.6 | % | SABIC Method | |
Mold Shrinkage, xflow, 3.2-4.6 mm | 0.6 - 1 | % | SABIC Method | |
ELECTRICAL | Value | Unit | Standard | |
Volume Resistivity | >3.4E+16 | Ohm-cm | ASTM D 257 | |
Dielectric Strength, in air, 3.2 mm | 19.2 | kV/mm | ASTM D 149 | |
Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | ASTM D 149 | |
Relative Permittivity, 100 Hz | 3.8 | - | ASTM D 150 | |
Relative Permittivity, 1 MHz | 3.7 | - | ASTM D 150 | |
Dissipation Factor, 100 Hz | 0.002 | - | ASTM D 150 | |
Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 | |
Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | |
High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A | |
High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
FLAME CHARACTERISTICS | Value | Unit | Standard | |
UL Recognized, 94V-0 Flame Class Rating (3) | 0.71 | mm | UL 94 | |
UL Recognized, 94-5VA Rating (3) | 2 | mm | UL 94 | |
CSA (See File for complete listing) | LS88480 | File No. | CSA LISTED | |
Oxygen Index (LOI) | 32 | % | ASTM D 2863 | |
UV-light, water exposure/immersion | F2 | - | UL 746C |
Source GMD, last updated:09/09/2008 |
Processing |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 120 | 掳C |
Drying Time | 3 - 4 | hrs |
Drying Time (Cumulative) | 12 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 255 - 275 | 掳C |
Nozzle Temperature | 250 - 270 | 掳C |
Front - Zone 3 Temperature | 255 - 275 | 掳C |
Middle - Zone 2 Temperature | 250 - 270 | 掳C |
Rear - Zone 1 Temperature | 245 - 265 | 掳C |
Mold Temperature | 65 - 90 | 掳C |
Back Pressure | 0.3 - 0.7 | MPa |
Screw Speed | 50 - 80 | rpm |
Shot to Cylinder Size | 40 - 80 | % |
Vent Depth | 0.025 - 0.038 | mm |