Lexan* Resin ML6411 | Americas: COMMERCIAL |
Lexan* ML6411 polycarbonate (PC) siloxane resin, is a high flow opaque injection molding (IM) grade with very low temperature ductility characteristics. This grade offers UL94 V0 @ 1.5mm and 5VA @ 3.0mm flame retardancy based on non-chlorine, non-bromine FR systems. Lexan ML6411 resin offers excellent processing characteristics with opportunity for shorter IM cycle times compared to standard PC. This product is available in a wide range of opaque colors and is an excellent candidate for a wide range of electrical applications. |
Property |
| TYPICAL PROPERTIES (1) | ||||
MECHANICAL | Value | Unit | Standard | |
Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 | |
Tensile Stress, brk, Type I, 50 mm/min | 54 | MPa | ASTM D 638 | |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 | |
Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D 638 | |
Tensile Modulus, 50 mm/min | 2500 | MPa | ASTM D 638 | |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 95 | MPa | ASTM D 790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2600 | MPa | ASTM D 790 | |
Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 | |
Tensile Stress, break, 50 mm/min | 58 | MPa | ISO 527 | |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 | |
Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 | |
Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 2350 | MPa | ISO 178 | |
IMPACT | Value | Unit | Standard | |
Izod Impact, notched, 23掳C | 900 | J/m | ASTM D 256 | |
Izod Impact, notched, -30掳C | 150 | J/m | ASTM D 256 | |
Instrumented Impact Total Energy, 23掳C | 72 | J | ASTM D 3763 | |
Izod Impact, notched 80*10*3 +23掳C | 60 | kJ/m虏 | ISO 180/1A | |
Izod Impact, notched 80*10*3 -30掳C | 15 | kJ/m虏 | ISO 180/1A | |
THERMAL | Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50 | 134 | 掳C | ASTM D 1525 | |
HDT, 1.82 MPa, 3.2mm, unannealed | 114 | 掳C | ASTM D 648 | |
HDT, 0.45 MPa, 6.4 mm, unannealed | 128 | 掳C | ASTM D 648 | |
HDT, 1.82 MPa, 6.4 mm, unannealed | 119 | 掳C | ASTM D 648 | |
CTE, -40掳C to 40掳C, flow | 7.7E-05 | 1/掳C | ASTM E 831 | |
CTE, -40掳C to 40掳C, xflow | 5.9E-05 | 1/掳C | ASTM E 831 | |
CTE, -40掳C to 40掳C, flow | 7.E-05 | 1/掳C | ISO 11359-2 | |
CTE, -40掳C to 40掳C, xflow | 7.E-05 | 1/掳C | ISO 11359-2 | |
Ball Pressure Test, 125掳C +/- 2掳C | PASSES | - | IEC 60695-10-2 | |
Vicat Softening Temp, Rate B/50 | 134 | 掳C | ISO 306 | |
Vicat Softening Temp, Rate B/120 | 135 | 掳C | ISO 306 | |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 125 | 掳C | ISO 75/Be | |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 115 | 掳C | ISO 75/Ae | |
Relative Temp Index, Elec | 100 | 掳C | UL 746B | |
Relative Temp Index, Mech w/impact | 100 | 掳C | UL 746B | |
Relative Temp Index, Mech w/o impact | 100 | 掳C | UL 746B | |
PHYSICAL | Value | Unit | Standard | |
Specific Gravity | 1.19 | - | ASTM D 792 | |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC Method | |
Melt Flow Rate, 260掳C/2.16 kgf | 7 | g/10 min | ASTM D 1238 | |
Density | 1.2 | g/cm鲁 | ISO 1183 | |
Water Absorption, (23掳C/sat) | 0.3 | % | ISO 62 | |
Moisture Absorption (23掳C / 50% RH) | 0.1 | % | ISO 62 | |
Melt Volume Rate, MVR at 260掳C/5.0 kg | 18 | cm鲁/10 min | ISO 1133 | |
ELECTRICAL | Value | Unit | Standard | |
Dielectric Strength, in oil, 3.2 mm | 26.5 | kV/mm | ASTM D 149 | |
Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A | |
High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A | |
Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
Volume Resistivity | > 1.E+15 | Ohm-cm | IEC 60093 | |
Comparative Tracking Index | 250 | V | IEC 60112 | |
FLAME CHARACTERISTICS | Value | Unit | Standard | |
UL Compliant, 94-5VA Rating (3)(4) | 3 | mm | UL 94 by GE | |
UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 | |
UL Recognized, 94-5VA Rating (3) | 3 | mm | UL 94 | |
UL Recognized, 94-5VB Rating (3) | 2 | mm | UL 94 | |
Glow Wire Flammability Index 960掳C, passes at | 1 | mm | IEC 60695-2-12 | |
Glow Wire Ignitability Temperature, 1.0 mm | 800 | 掳C | IEC 60695-2-13 | |
Glow Wire Ignitability Temperature, 2.0 mm | 800 | 掳C | IEC 60695-2-13 | |
Glow Wire Ignitability Temperature, 3.0 mm | 800 | 掳C | IEC 60695-2-13 | |
Source GMD, last updated:10/06/2004 |
Processing |
| Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 90 - 100 | 掳C |
Drying Time | 2 - 4 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 270 - 300 | 掳C |
Nozzle Temperature | 250 - 290 | 掳C |
Front - Zone 3 Temperature | 260 - 300 | 掳C |
Middle - Zone 2 Temperature | 250 - 290 | 掳C |
Rear - Zone 1 Temperature | 230 - 260 | 掳C |
Hopper Temperature | 60 - 80 | 掳C |
Mold Temperature | 60 - 90 | 掳C |
Source GMD, last updated:10/06/2004 |