Noryl GTX* Resin GTX973 | Americas: COMMERCIAL |
NORYL GTX973 is a material especially designed for electrostatic painting and powder coating applications. The material combines high heat resistance with impact and conductivity in a unique way. |
Property |
TYPICAL PROPERTIES (1) | ||||
MECHANICAL | Value | Unit | Standard | |
Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D 638 | |
Tensile Stress, brk, Type I, 50 mm/min | 55 | MPa | ASTM D 638 | |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 | |
Tensile Strain, brk, Type I, 50 mm/min | 55 | % | ASTM D 638 | |
Tensile Modulus, 50 mm/min | 2200 | MPa | ASTM D 638 | |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 90 | MPa | ASTM D 790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2300 | MPa | ASTM D 790 | |
Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 | |
Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 | |
Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 | |
Tensile Strain, break, 50 mm/min | 30 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 | |
Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 | |
IMPACT | Value | Unit | Standard | |
Izod Impact, notched, 23掳C | 130 | J/m | ASTM D 256 | |
Izod Impact, notched, -30掳C | 80 | J/m | ASTM D 256 | |
Instrumented Impact Total Energy, 23掳C | 50 | J | ASTM D 3763 | |
Izod Impact, notched 80*10*4 +23掳C | 15 | kJ/m虏 | ISO 180/1A | |
Izod Impact, notched 80*10*4 -30掳C | 7 | kJ/m虏 | ISO 180/1A | |
Charpy 23掳C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m虏 | ISO 179/1eA | |
Charpy -30掳C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m虏 | ISO 179/1eA | |
THERMAL | Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50 | 200 | 掳C | ASTM D 1525 | |
HDT, 0.45 MPa, 3.2 mm, unannealed | 195 | 掳C | ASTM D 648 | |
CTE, -40掳C to 40掳C, flow | 8.5E-05 | 1/掳C | ASTM E 831 | |
CTE, -40掳C to 40掳C, xflow | 9.E-05 | 1/掳C | ASTM E 831 | |
CTE, 23掳C to 60掳C, flow | 9.E-05 | 1/掳C | ISO 11359-2 | |
CTE, 23掳C to 60掳C, xflow | 9.E-05 | 1/掳C | ISO 11359-2 | |
Ball Pressure Test, 125掳C +/- 2掳C | PASSES | - | IEC 60695-10-2 | |
Vicat Softening Temp, Rate B/50 | 195 | 掳C | ISO 306 | |
Vicat Softening Temp, Rate B/120 | 200 | 掳C | ISO 306 | |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 190 | 掳C | ISO 75/Be | |
PHYSICAL | Value | Unit | Standard | |
Specific Gravity | 1.09 | - | ASTM D 792 | |
Mold Shrinkage, flow, 3.2 mm | 1.4 - 1.7 | % | SABIC Method | |
Mold Shrinkage, xflow, 3.2 mm | 1.2 - 1.5 | % | SABIC Method | |
Melt Flow Rate, 280掳C/5.0 kgf | 20 | g/10 min | ASTM D 1238 | |
Density | 1.1 | g/cm鲁 | ISO 1183 | |
Water Absorption, (23掳C/sat) | 4.2 | % | ISO 62 | |
Moisture Absorption (23掳C / 50% RH) | 1.2 | % | ISO 62 | |
Melt Volume Rate, MVR at 280掳C/5.0 kg | 12 | cm鲁/10 min | ISO 1133 | |
ELECTRICAL | Value | Unit | Standard | |
Volume Resistivity | 1.E+03 - 1.E+04 | Ohm-cm | SABIC Method |
Source GMD, last updated:06/25/2007 |
Processing |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 100 - 120 | 掳C |
Drying Time | 2 - 3 | hrs |
Maximum Moisture Content | 0.07 | % |
Melt Temperature | 290 - 320 | 掳C |
Nozzle Temperature | 280 - 310 | 掳C |
Front - Zone 3 Temperature | 290 - 320 | 掳C |
Middle - Zone 2 Temperature | 280 - 300 | 掳C |
Rear - Zone 1 Temperature | 260 - 280 | 掳C |
Hopper Temperature | 60 - 80 | 掳C |
Mold Temperature | 80 - 120 | 掳C |